Based on experimental results that VH0.81/MgH2 interface was found during the process of mechanically milling MgH2+5at.%V nanocomposite, H atoms diffusion and adsorption properties of MgH2-V systems have been investigated by using a first-principles plane-wave pseudopotential method based on the density functional theory. The results are as follows. When VH/MgH2 interface is formed due to V alloying MgH2 phase, the vacancy formed by H atoms near VH phase region is more stable than that without V alloying, while vacancy near MgH2 phase region is less stable than that without V alloying. During the process of H atoms diffusion after V alloying, the max migration barrier energy of H atoms in MgH2-V systems is reduced compared with that of MgH2 phase, which means that H atoms diffuse easily. When H diffuses into VH from MgH2 across VH/MgH2 interface, among three substitutions such as the replacement of H for V vacancy, or interstitial site or V atoms, the replacement of H for V vacancy has the strongest diffusion ability, next interstitial site, and finally V atoms site. As far as H adsorbed on different surfaces of VH phase is concerned, physical adsorption is carried out more easily than chemical adsorption, and the behavior of H atoms adsorbed on the surface near VH phase region can be found more easily than that near MgH2 phase region.
ZHOU DianWu1,2, LIU JinShui3 & PENG Ping3 1 State Key Laboratory of Advanced Design and Manufacturing for Vehicle Body, Hunan University, Changsha 410082, China
With the aid of the molecular orbital DMol3 program,the energetics and electronic structures of several AlnC（n = 2-7） configurations have been searched and calculated by improved minimum energy paths（MEPs） by setting ＂imaging product＂.A new high symmetry,supervalence isomer of Al5C cluster,i.e.,D5h-Al5C,at the local minimum in the MEPs is detected.Several parameters,such as binding energy,HOMO-LUMO energy gap,vertical electron detachment energy and electron affinity energy,are calculated to characterize and evaluate the stability of three Al5C configurations,i.e.,D5h-Al5C,Cs-Al5C and C1-Al5C.The results show that the D5h-Al5C cluster is the ground state structure instead of Cs-Al5C.Due to the formation of many central σ bonds after polymerizing for D5h-Al5C,the decrease of the energy for HOMO orbit results in more territory for HOMO electrons of dislocation effect,then the energy difference between HOMO and LUMO is increasing to enhance the stability of molecules to produce such supervalence structure of Al5C cluster.The configuration evolution between D5h-Al5C,Cs-Al5C and C1-Al5C and the synthesis preference in the mode of Al5 ＋ C → Al5C reveals that the Cs-Al5C and C1-Al5C con-figurations are permissive to coexist with D5h-Al5C structure in energetics.