Phase evolution and room temperature ferroelectric and magnetic properties of Fe-doped BaTiO_3 ceramics被引量：4: 2010年; To make the ferroelectric BaTiO3 possess ferromagnetism simultaneously,magnetic Fe was doped into BaTiO3 ceramics at doping levels up to 10%(molar fraction).Both tetragonal and hexagonal phases coexisted in the Fe-doped BaTiO3 ceramics except at 1% doping level.X-ray diffraction analysis indicated that higher doping level of Fe,higher sintering temperature and longer sintering time promoted the formation of hexagonal phases in Fe-doped BaTiO3 ceramics.Ferroelectricity was observed in all samples at room temperature,but it was greatly depressed by Fe doping.Except at doping level of 1%,room-temperature ferromagnetism was observed in the BaTiO3 ceramics.The dependence of the saturation magnetization and coercivities of the Fe-doped BaTiO3 ceramics on doping level was systematically studied.Both the saturation magnetization and magnetic coercivities were found to be dependent on the doping level as well as the fraction of the hexagonal phase in the ceramics.; 邱深玉李旺刘宇刘桂华吴毅强陈楠; 关键词：FERROELECTRICITY MAGNETISM

碳纳米管导电纸制备及其电磁屏蔽性能研究被引量：3: 2014年; 研究了一种新型柔性碳纳米管复合导电纸。以纸纤维作为载体,晶须状碳纳米管为导电剂,通过高速剪切的方法制备纸纤维与碳纳米管悬浮液,使碳纳米管均匀分散并吸附在纸纤维。经过真空抽滤,悬浮液均匀沉降形成致密的纤维网。烘干后轧制成碳纳米管-纸纤维复合导电纸。采用扫描电子显微镜、四探针电阻仪、矢量网络分析仪对其进行表征。研究表明当纸纤维和碳纳米管加载比为1∶1时,碳纳米管导电纸表面电阻可达28Ω/□,体积电阻率可达2.32Ω·cm。在175~2700 MHz频段,碳纳米管导电纸电磁屏蔽效能为-18^-31 dB,多层碳纳米管导电屏蔽效能可达-24^-37 dB。; 庞志鹏孙晓刚程晓圆曹宏辉吴小勇付琦; 关键词：碳纳米管纸纤维导电纸电磁屏蔽

柔性碳纳米管复合导电纸的制备及其在锌锰纸电池中的应用: 2015年; 以碳纳米管和纸纤维混合制成均匀液体经抽滤制备成复合导电纸。采用不同工艺将石墨化碳纳米管和纸纤维复合,通过四探针电阻仪表征表面电阻和XRD、TEM、SEM等表征内部结构。将制备的导电纸作为集流体,采用CT-3008W-5V5m A-S4检测仪测试锌锰纸电池电化学性能。结果表明,当碳纳米管与纸浆质量比为2∶1时,表面电阻为20Ω/□,碳纳米管与纸纤维复合效果最佳。使用碳纳米管导电纸作集流体时,和石墨集流体相比,放电时间增加36.7%~122.4%,电池质量能量密度提高64.1%~141%。碳纳米管导电纸作集流体能大幅提高电池的能量密度。; 吴小勇孙晓刚庞志鹏付琦程晓圆; 关键词：碳纳米管二氧化锰

碳纳米管在1～6GHz频段的电磁波屏蔽性能被引量：5: 2010年; 研究了碳纳米管高频电磁波的屏蔽性能。碳纳米管经微波处理后在丙酮中经高速剪切分散,再加入到硅橡胶中经超声和搅拌分散制成试样。采用扫描电镜(SEM)观测碳纳米管在基体中的分散状况,采用AV3620型矢量网络分析仪检测电磁屏蔽性能。研究显示,随着碳纳米管加载量的增加,试样的导电性能和电磁屏蔽性能均得到改善。碳纳米管加载量达到12%(质量分数,下同)时,试样的表面电阻率下降9个数量级,减小到103Ω,电磁屏蔽性能大幅提高。在1~6GHz频率范围内,屏蔽效能达到-30^-42dB。; 孙晓刚程利高明吴毅强杜国平; 关键词：碳纳米管电磁屏蔽吸波材料功能材料

碳纳米管对五氯苯酚的吸附性能研究: 2016年; 研究了多壁碳纳米管对难降解的多氯代有机产物-五氯苯酚的吸附特性,并采用电子扫描电镜、多波长紫外吸收测量仪对其进行了表征分析。结果表明,碳纳米管经酸化纯化预处理后,表面光滑无杂质,出现许多新端口,大大地提高了其对五氯苯酚（PCP）的吸附效果;碳纳米管对PCP在波长为217、255、323nm处都有强紫外吸收;在λ=217nm处,PCP甲醇溶液浓度与吸光度值之间具有良好的线性关系,相关度r^2=0.9999,线性范围为0.386-4.045mg/L。多壁碳纳米管对PCP的吸附符合Freundlich吸附等温模型,随着初始浓度增加,吸附量增加,随着温度升高,吸附量降低。; 程晓圆孙晓刚聂艳艳庞志鹏; 关键词：多壁碳纳米管五氯苯酚紫外光谱

电磁屏蔽硅橡胶研制: 采用超声和高速搅拌将碳纳米管均匀地分散在硅橡胶基体中,制备碳纳米管/硅橡胶复合电磁屏蔽材料。碳纳米管和碳纳米管复合材料的结构和形貌通过扫描电镜(SEM)和投射电镜(TEM)观测,复合材料电池屏蔽性能采用AV3620型矢量...; 程利孙晓刚高明; 关键词：碳纳米管硅橡胶复合材料电磁屏蔽; 文献传递

阵列式碳纳米管雷达波吸收性能研究被引量：14: 2009年; 研究了阵列式碳纳米管的雷达波吸收性能。采用化学气相沉积(CVD)工艺制备阵列式碳纳米管薄膜,并采用SEM和TEM对其进行观测。观测显示:阵列式碳纳米管薄膜中碳纳米管排列规则,有很好的定向性,直径30～50nm。阵列式碳纳米管薄膜平铺在铝板上并用环氧树脂固定制成试样,采用反射率扫频测量系统HP8757E矢量网络分析仪检测阵列式碳纳米管吸波性能。结果表明:阵列式碳纳米管在2～18GHz频段的较高频段表现出良好的吸波性能。吸波性能随薄膜厚度不同而改变。阵列式碳纳米管薄膜厚度为0.2mm时,雷达波吸收性能最佳,峰值R为-15.87dB,波峰出现在17.83GHz,带宽分别为4.25GHz(R<-10dB)和6.40GHz(R<-5dB)。; 孙晓刚程利杜国平; 关键词：阵列式碳纳米管纳米吸波材料

十八胺改性碳纳米管导电纸的性能研究被引量：3: 2013年; 以多壁碳纳米管为导电剂,通过十八胺修饰改性,使用常规印刷技术,将经过十八胺修饰后的碳纳米管沉积于纸纤维网络上,制成可运用于电子器件的碳纳米管导电纸,并运用扫描电子显微镜、矢量网络分析仪、红外光谱仪与表面电阻测量仪对其进行表征。结果表明,经过十八胺修饰过的碳纳米管,其分散性能提高,表面电阻率大幅度下降,电磁屏蔽性能大幅提高。; 曹宏辉孙晓刚王健姚军高明; 关键词：碳纳米管电磁屏蔽十八胺导电纸

锰酸锂改性及其电化学性能研究被引量：2: 2011年; 以多壁碳纳米管(Multi-walled carbon nanotubes,MWCNTs)为添加相,对锰酸锂进行电化学性能改进,采用扫描电子显微镜对其进行观察,发现掺入的多壁碳纳米管均匀分布在锰酸锂颗粒表面。以改性后的锰酸锂为主要材料制成纽扣电池,采用交流阻抗及恒电流充放电等技术进行检测。结果表明,掺入1%MWCNTs后LiMn2O4的初始放电容量由改性前的123mAh/g下降到改性后的117mAh/g,在25℃经10次循环后容量保持率为97%,明显高于未掺入的91%。与未掺杂的LiMn2O4相比,虽然掺C或掺CNTs都使初始充放电容量有所降低,但是其循环性能明显提高。; 高明孙晓刚程利吁霁; 关键词：锰酸锂多壁碳纳米管循环性能

碳纳米管纸作集流体在柔性锌锰电池中的应用被引量：1: 2016年; 研究了晶须状碳纳米管导电纸作为集流极对锌锰电池放电性能的影响。使用晶须状碳纳米管(MWCNTs),通过抽滤法制备出碳纳米管纸,利用扫描电子显微镜(SEM)对碳纳米管导电纸进行表征。碳纳米管导电纸作为柔性锌锰电池集流体,正极极片采用二氧化锰为活性材料,负极采用金属锌为电极,使用计算机控制精密电池测试仪测试其电化学性能。实验表明,柔性锌锰电池具有良好的机械柔性,弯曲状依旧保持电压稳定。与采用石墨为集流体的传统锌锰电池相比,在0.3mA恒流放电的情况下,碳纳米管纸作为集流体,锌锰电池的放电时间增加了64.2%,比容量提高186%,比能量提高172%。碳纳米管纸作为集流体的柔性锌锰电池表现出极佳优越性,并且碳纳米管纸的密度对电池放电性能有着较大的影响。; 付琦孙晓刚程晓圆庞志鹏吴小勇; 关键词：锌锰电池集流体

渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心　互联网出版许可证　新出网证(渝)字10号

国家自然科学基金(60661001)

文献类型

领域

主题

机构

作者

传媒

年份

用户反馈

国家自然科学基金(60661001)

文献类型

领域

主题

机构

作者

传媒

年份

用户登录

用户反馈