Warm deformation was investigated for steels containing carbon of 0. 45%,0. 79%, and 1. 26% respeetively with martensite starting structure, using Gleeble 3500 thermomechanical simulator at the temperature ranging from 873 K to 973 K and the strain rate ranging from 0.1 s^-1 to 0. 001 s^-1. The effect of carbon content on the deformation activation energy, Z value and the deformation resistance was analyzed, The results showed that the deformation resistance decreased with increasing carbon content. The peak stress of the steel containing earbon of 1.26% was decreased by 16.2% compared to the steel containing carbon of 0.45% under the same condition. This may be attributed to the weakening effect of solid solution strengthening which outweighs the precipitation strengthening of cementite.
LI Qun WANG Tian-sheng LI Hong-biao GAO Yu-wei LINing JING Tian-fu