Uniform ZnO toothed-nanobelts and nanocombs were fabricated respectively through pure zinc powder evaporation without catalyst at temperature of 600-650℃. Scanning electron microscopy （SEM） and high-resolution transmission electron microscopy （HRTEM） observations show that such ZnO nanostructures have several types in morphology, and all of them are single crystalline. The experimental results reveal that the growth of the ZnO nanostructures was controlled by vapor-solid mechanism. Room temperature photoluminescence spectra of the toothed-nanobelts show a UV emission at - 390 nm and a broad green emission with 4 subordinate peaks at 455-495 nm.
Fe100-xPtx(x=30at.%-60at.%) nanocomposite films were deposited on natural-oxidized Si(100) substrates by magnetron sputtering. The as-deposited films were annealed between 373 and 1073 K. In situ X-ray diffraction shows that the FePt nanocomposite films undergo a phase transformation from a disordered FCC phase to an ordered L10 phase between 673 and 773 K. The coercivity is 306 kA·m-1 whiles the average grain sizes is about 10 nm in the optimized FePt alloy film sample annealed at 673 K. The adjustable coercivity and fine grain size suggest that this FePt nanocomposites system is suitable as recording media at extremely high areal density.