In this study,an excellent polarization optical crystal LiNa_(5)Mo_(9)O_(30) with wide transmission range and high laser damage threshold was researched in detail.The laser damage threshold of the LiNa_(5)Mo_(9)O_(30) crystal was measured to be 2.64GW/cm^(2),which was the highest among polarized optical crystals.The birefringence in the range of 0.435-5μm was larger than 0.14,while the wedge angle between 31.94°and 32.12°would satisfy the application in this waveband.The extinction ratio of the fabricated prism with the wedge angel of 31.09°was larger than 15,000:1.The results show that the LiNa_(5)Mo_(9)O_(30) prism is an excellent polarization device,especially in the mid-infrared range and high-power applications.
Xiaoli DuZeliang GaoLijuan ChenYouxuan SunXutang Tao
Hierarchical porous patterns have been fabricated on the C face, Si face, and cross section of n-type 6H-SiC crystal via photo-electrochemical etching using HF/C2H5OH and HF/H2O2 as electrolytes. The porous layer displayed multiple and multiscale microstructures on different faces, including stalactite-like, sponge-like and dendritic porous structures on C face, echinoid micro-patterns on Si face, and columnar and keel-shaped micro-patterns on the cross section. The formation of hierarchical porous pattern is ascribed to the dynamic competition balance between the electrochemical oxidation rate and the oxide removal rate. It was found that increasing the ionic strength of the electrolyte can obviously disturb the surface morphology of the porous SiC during the photo-electrochemical etching. Possible mechanisms for selective etching were further discussed.