The physical-mechanical properties of Populus x canadensis Moench and Populus x euramericana （Dode） Guinier cv. Gelrica were studied to provide theoret- ical and scientific bases for the directional breeding and efficient use of artificial forests with P. canadensis and P. euramericana Gelrica. The results showed the air-dried density, basic density of P. canadensis were 0.468 g/cm3 and 0.372 g/cm3, respectively; the shrinkage coefficient of radial, tangential and volume were 0.133%, 0.270% and 0.553%, respectively;the modulus of elasticity in static bending, the bending strength and the compressive strength parallel to grain were 9 302.99 MPa, 79.69 MPa and 40.32 Mpa, respectively. As for the P. euramericana Gelrica, the air-dried density, basic densitywere 0.453 and 0.355 g/cm3, respectively; the shrink- age coefficient of radial, tangential and volume were 0.205%, 0.304% and 0.554%, respectively; the modulus of elasticity in static bending, the bending strength and the compressive strength parallel to grain were 9 014.44, 55.87 and 33.09 Mpa respectively. Comprehensive analysis of the indicators showed that the properties of P. canadensis were better than those of P.euramericana Gelrica.