Ce0.8Sm0.2O1.9-δ-La0.9Sr0.1Ga0.8Mg0.2O3-δ（SDC-LSGM）is prepared by the glycine-nitrate process（GNP）.SDC-LSGM composite electrolyte samples with different weight ratios are prepared by the co-combustion method so as to obtain homogeneous nano-sized precursor powders. The X-ray diffraction （XRD） and the scan electron microscope （SEM） are used to investigate the phases and microstructures. The measurements and analyses of oxygen ionic conductivity of SDC-LSGM are carried out through the four-terminal direct current （DC） method and the electrochemical impendence spectroscopy, respectively. The optimum weight ratio of SDC-LSGM is 8∶2, of which the ionic conductivity is 0.113 S/cm at 800℃ and the conductivity activation energy is 0.620 eV. The impendence spectra shows that the grain boundary resistance becomes the main barrier for the ionic conductivity of electrolyte at lower temperatures. The appropriate introduction of LSGM to the electrolyte SDC can not only decrease the electronic conductivity but also improve the conditions of the grain and grain boundary, which is advantageous to cause an increase in oxygen ionic conductivity.