The metal complex 5-（4-aminophenyl）-10,15,20-triphenylporphyrin copper （CuAPTPP） was covalently linked on the surface of TiO2 microspheres by using toluene disocyanate （TDI） as a bridging bond unit. The hydroxyl group （-OH） of TiO2 microspheres surface and the amino group （-NH2） of CuAPTPP reacted respectively with the active -NCO groups of TDI to form a surface conjugated microsphere CuAPTPP-TDI-TiO2 that was confirmed by FT-IR spectra. The CuAPTPP-TDI-TiO2 microspheres were characterized with UV-visible, elemental analysis, XRD, SEM, and UV-Vis diffuse reflectance spectra. The effect of amounts of linked TDI on the performance of photocatalytic microspheres was discussed, and the optimal molar ratio of TDI：TiO2 was established. The photocatalytic activity of CuAPTPP- TDI-TiO2 was evaluated using the photocatalytic degradation of methylene blue （MB） under visible-light irradiation. The results showed that, TDI, as a bond unit, was used to form a steady chemical brigdging bond linking CuAPTPP and the surface of TiO2 microspheres, and the prepared catalyst exhibited higher photocatalytic activity under visible-light irradiation for MB degradation. The degradation rate of 20 mg/L MB could reach 98.7% under Xe- lamp （150 W） irradiation in 120 rain. The degradation of MB followed the first-order reaction model under visible light irradiation, and the rate constant of 5.1× 10^-2 min-1 and the half- life of 11.3 min were achieved. And the new photocatalyst can be recycled for 4 times, remaining 90.0% MB degradation rate.