Branched polyethylene from ethylene as single monomer was prepared by the tandem catalyst system of {2-[2-Me C6H4 N（Me）]2C5H3N}FeCl2（1） and {2,6-[1-(2,6-Me2-4-Br-C6H4N（Me）]2C5H3N} FeCl2（2） activated with methylaluminoxane （MAO） .The products of polymerization were characterized by DSC,GPC and （）13C-NMR.The results revealed that the copolymer produced by in situ copolymerization of ethylene was a mixture of branched polyethylene and α-olefin.The content of α-olefin in the mixture was increased with increasing the molar ratio of catalysts 1/2.The MWD paramelers of polyethylene and copolymer were 28\^6 and 7\^9, respectively.（）13C-NMR spectra showed that there were ethyl groups,butyl groups and long chain alkyl groups in the copolymer.The average degree of branching of such branched polyethylene was less than 5C/1000C.