Mg65Cu25Y10 bulk amorphous alloy specimens prepared by conventional copper mould method were heated at 200 °C for different time and the phase contents as well as microstructure were studied.The XRD results show that the crystallization of Mg65Cu25Y10 bulk amorphous alloy specimen becomes complete as the treating time increases and Mg2Cu,Mg24Y5 and HCP-Mg crystalline phases are found.Snowflake-like morphology is found in different specimens through SEM observation.The EDS patterns show that the composition of the snowflake-like structure is close to that of the as-cast alloy.Laminated structures are observed from the TEM images of the snowflake-like structure.From the electron diffraction patterns,it is seen that the snowflake-like structure is the combination of Mg24Y5 and amorphous matrix.The FCC-Mg phase in the matrix transforms into HCP-Mg during the heat-treating process.
The influence of solution treatment on the microstructure and properties of Mg2Si/AZ91D composites fabricated from Mg-SiO2 system via in-situ processing method was investigated.The results show that coarse Chinese script shape Mg2Si phases can be formed by adding SiO2 into AZ91D magnesium alloy with Si content up to 1.5% of the alloy melt.During solution treatment,the morphology and distribution of the coarse Chinese script shape Mg2Si phases are modified.Meanwhile,the β-Mg17Al12 phase is dissolved into the magnesium matrix.With increasing holding time,the coarse Mg2Si phases tend to dissolve,break and spheroidize.After solution treatment at 420 ℃ for 16 h,Mg2Si phases become the finest and relatively well-distributed phase.The tensile strength and elongation are increased by 14.9% and 38.9%,respectively.It is believed that the Mg2Si phases continuously dissolve and break,and finally the spheroidized Mg2Si particles are obtained due to the interface tension of Mg2Si/Mg interface.